Akturk, Omer; Keskin, Dilek
{ "DOI": "10.3906/biy-1502-49", "abstract": "As a novel approach in skin tissue engineering, gold nanoparticles (AuNPs) were synthesized and incorporated at different concentrations into collagen/PEO nanofibrous matrices in this study. The group containing 14.27 ppm AuNPs (CM-Au) had the best nanofibrous morphology. CM-Au was cross-linked with glutaraldehyde vapor (CM-AuX). All groups were disrupted in collagenase in 2 h, but cross-linked groups and Matriderm (R) resisted hydrolytic degradation for 7 and 14 days, respectively. Due to its small pores and dense structure, lower water swelling results (7.26 +/- 2.62 g/g) were obtained for CM-AuX than Matriderm (17.51 +/- 1.97 g/g). CM-Au and Matriderm had statistically similar tensile strength and elastic modulus, but elongation at break of CM-Au (over 100%) was significantly better than that of Matriderm. After cross-linking, tensile strength and elastic modulus of collagen matrix was further improved. AuNPs (37 and 42 nm) seemed to be nontoxic on 3T3 fibroblasts and keratinocytes for different time periods. CM-AuX scaffold extracts were also nontoxic for 3T3 fibroblasts and keratinocytes. The L929 cell attachment and proliferation on CM-AuX were comparable with Matriderm, indicating good in vitro biocompatibility. As a whole, collagen matrices incorporated with AuNPs are potential biomaterial candidates for skin tissue engineering.", "author": [ { "family": "Akturk", "given": " Omer" }, { "family": "Keskin", "given": " Dilek" } ], "container_title": "TURKISH JOURNAL OF BIOLOGY", "id": "58535", "issue": "2", "issued": { "date-parts": [ [ 2016, 1, 1 ] ] }, "page": "380-398", "title": "Collagen/PEO/gold nanofibrous matrices for skin tissue engineering", "type": "article-journal", "volume": "40" }
Görüntülenme | 32 |
İndirme | 12 |
Veri hacmi | 62.5 MB |
Tekil görüntülenme | 31 |
Tekil indirme | 12 |