Enhanced Electrical Properties of P3HT:WO3 Hybrid Thin Film Transistors

   Yedikardes, Beyza; Ordokhani, Fereshteh; Akkan, Nihat; Kurt, Ece; Yavuz, Nilgun Karatepe; Zayim, Esra; Altun, Mustafa

In recent decades, conjugated polymers have been widely studied in organic electronics to produce low-cost transistors. Additionally, these polymers are doped with inorganic materials in order to improve the transistor performance in terms of mobility, on/off current ratio, and threshold voltage as well as to ease processability. In this study, we use various doping concentrations (0-50% in weight) of tungsten oxide (WO3) in poly(3-hexylthiophene) (P3HT), a well-studied organic semiconductor, to optimize the transistor performance. We treat spin-coated film of the hybrid P3HT:WO3 solution on hexamethyl disilazane (HMDS) as channels of commercial test chips including 20 transistors with their gold electrodes. Compared to using pristine P3HT, the proposed hybrid P3HT:WO3 formula which significantly improves the transistor performance. Almost 105 times larger mobilities, almost 10 times larger on/off current ratios, and nearly 22 V decrease in threshold voltages were achieved. It was also observed that the excess amount of WO3 doping leads to worse mobilities and on/off current ratios.

Dosyalar (216 Bytes)
Dosya adı Boyutu
bib-1d98e6e8-0c4a-4c83-b19c-a76ab14aa503.txt
md5:2d86fbc54cd7a28d6c4f507cc76f147e
216 Bytes İndir
21
7
görüntülenme
indirilme
Görüntülenme 21
İndirme 7
Veri hacmi 1.5 kB
Tekil görüntülenme 20
Tekil indirme 7

Alıntı yap