  <datafield tag="520" ind1=" " ind2=" ">
    <subfield code="a">The thermal degradation of graphite and glass-reinforced phenolic insulators have been studied at high temperature by using thermogravimetric (TGA) and differential scanning calorimetric analyses. TGA analysis was carried out in a stream of pure nitrogen over temperature range ambient to 900 degrees C and DSC analysis to 500 degrees C. A heating rate of 10 degrees C/min was used for the determination of degradation temperature and heating rates of 5, 10, 20, 30, and 50 degrees C/min were used for the estimation of degradation temperature (T-max) of the insulator at high-temperature service and calculation of activation. Activation energy of phenolic resin was calculated as 356 kJ mol(-1) using the Ozawa method. T-max was determined as 661 degrees C for 20% conversion. The specific heat capacity of graphite phenolic was found as 970 J kg(-1) K-1 at 100 degrees C. The half-life of the phenolic resin was determined to be approximately 116.2 s at 3500 degrees C. The thermal analysis has been conducted using transient heat conduction and the in-depth temperature distribution was evaluated along the rocket nozzle. The better insulator thickness, including a safety factor for graphite and E-glass-reinforced phenolics were calculated as 3 and 2 mm, respectively. (C) 1998 John Wiley &amp;amp; Sons, Inc.</subfield>
  </datafield>
  <datafield tag="980" ind1=" " ind2=" ">
    <subfield code="a">publication</subfield>
    <subfield code="b">article</subfield>
  </datafield>
  <datafield tag="540" ind1=" " ind2=" ">
    <subfield code="a">Creative Commons Attribution</subfield>
    <subfield code="u">http://www.opendefinition.org/licenses/cc-by</subfield>
  </datafield>
  <datafield tag="773" ind1=" " ind2=" ">
    <subfield code="i">isVersionOf</subfield>
    <subfield code="a">10.81043/aperta.102768</subfield>
    <subfield code="n">doi</subfield>
  </datafield>
  <datafield tag="100" ind1=" " ind2=" ">
    <subfield code="a">Pektas, I</subfield>
  </datafield>
  <datafield tag="856" ind1="4" ind2=" ">
    <subfield code="z">md5:4fcdc2ea32a81803c5cd3610c82ff52f</subfield>
    <subfield code="s">135</subfield>
    <subfield code="u">https://aperta.ulakbim.gov.trrecord/102769/files/bib-a24e0239-7415-48f7-8d3f-08293f2fa0bf.txt</subfield>
  </datafield>
  <controlfield tag="005">20210316145805.0</controlfield>
  <datafield tag="260" ind1=" " ind2=" ">
    <subfield code="c">1998-01-01</subfield>
  </datafield>
  <datafield tag="024" ind1=" " ind2=" ">
    <subfield code="a">10.81043/aperta.102769</subfield>
    <subfield code="2">doi</subfield>
  </datafield>
  <datafield tag="542" ind1=" " ind2=" ">
    <subfield code="l">open</subfield>
  </datafield>
  <datafield tag="245" ind1=" " ind2=" ">
    <subfield code="a">High-temperature degradation of reinforced phenolic insulator</subfield>
  </datafield>
  <datafield tag="909" ind1="C" ind2="4">
    <subfield code="v">68</subfield>
    <subfield code="p">JOURNAL OF APPLIED POLYMER SCIENCE</subfield>
    <subfield code="c">1337-1342</subfield>
    <subfield code="n">8</subfield>
  </datafield>
  <datafield tag="650" ind1="1" ind2="7">
    <subfield code="a">cc-by</subfield>
    <subfield code="2">opendefinition.org</subfield>
  </datafield>
  <controlfield tag="001">102769</controlfield>
  <datafield tag="980" ind1=" " ind2=" ">
    <subfield code="a">user-tubitak-adresli-yayinlar</subfield>
  </datafield>
</record>