Auwal, I. A.; Erdemi, H.; Sozeri, H.; Gungunes, H.; Baykal, A.
{ "DOI": "10.1016/j.jmmm.2016.03.066", "abstract": "In the present study, SrBixFe12-xO19 (0.0 <= x <= 1.0) nanomaterials were successfully synthesized by using chemical co-precipitation method. Products were characterized by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), Vibrating sample magnetometer (VSM), Mossbauer spectroscopy, AC conductivity and dielectric measurements. The crystal structural information studied by X-ray diffraction (XRD) indicated the formation of single phase pure hexagonal structure, while electron-dispersive X-ray spectroscopy (EDX) revealed the stoichiometric ratio among Bi, Sr, Fe elements. The crystallite sizes of the products were in the range of 65-82 nm. VSM analysis showed a tendency in saturation magnetization as Bi2O3 concentration raises, which can be ascribed to preferential site occupied by Bi3+ ions. The frequency-dependent ac conductivity plots exhibited similar trends for all samples. A significant temperature-dependent behavior was only observed at low and medium frequencies. The replacement of non-magnetic Bi3+ ions by Fe3+ ones having magnetic moment of 5 mu B decrease the magnetic moment of 4f1 site. The AC conductivity increases with frequency as hopping of the charge carriers increases between Fe2+ and Fe3+ The DC conductivity exhibited an improvement with increasing temperature and Bi content, and the highest conductivity was measured as 2.84 x 10(-9) S cm(-1) for x=0.8 at 120 degrees C. The variation of dielectric constant, dielectric loss and tangent loss was observed with the frequency and temperature due to change of electrical conductivity as x changes. (C) 2016 Elsevier B.V. All rights reserved.", "author": [ { "family": "Auwal", "given": " I. A." }, { "family": "Erdemi", "given": " H." }, { "family": "Sozeri", "given": " H." }, { "family": "Gungunes", "given": " H." }, { "family": "Baykal", "given": " A." } ], "container_title": "JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS", "id": "98693", "issued": { "date-parts": [ [ 2016, 1, 1 ] ] }, "page": "69-82", "title": "Magnetic and dielectric properties of Bi3+ substituted SrFe12O19 hexaferrite", "type": "article-journal", "volume": "412" }
Görüntülenme | 22 |
İndirme | 6 |
Veri hacmi | 1.3 kB |
Tekil görüntülenme | 22 |
Tekil indirme | 6 |