The investigation of the tribocorrosion properties of DLC coatings deposited on Ti6Al4V alloys by CFUBMS

Various machine components produced from titanium alloys used in various industries are subject to a combination of electrochemical and mechanical effects. The science of surface transformations resulting from the interaction of mechanical loading and chemical reactions that occur between elements of a tribosystem exposed to corrosive environments is described as tribocorrosion. This research focuses on the tribocorrosion behaviour of Ti6Al4V alloys after coated by using closed field unbalance magnetron sputtering (CFUBMS). The structural analyses of the coatings were performed using Raman spectroscopy and scanning electron microscopy (SEM). Tribocorrosion experiments were performed in a pin-on-disc tribotester under electrochemical polarisation in NaCI 1 wt.% solution. This study shows that the Ti-DLC coating is protecting the Ti6Al4V alloy and having good performance in corrosion and tribocorrosion conditions. The OCP values for Ti6Al4V substrate and Ti-DLC protective coatings during tribocorrosion tests were measured as -560V and -330V, respectively. These results showed that Ti-DLC protective coating on Ti6Al4V substrates increased the tribocorrosion resistance by acting as a barrier layer. (C) 2011 Elsevier B.V. All rights reserved.