The performance studies on swallow-tailed naphthalene diimide derivatives in solution processed inverted bulk heterojunction solar cells

  • 1. Ege Univ, Solar Energy Inst, TR-35100 Bornova, Turkey

Description

Two different soluble swallow-tailed naphthalene diimide derivatives were synthesized, 1,4:5,8-naphthalene diimides (NDIs), N,N'-bis-(1-butylpentyI)-naphthalenetetracarboxylic-1,4:5,8-biscarboximide (NDI-1) and N,N'-bis-(1-pentylhexyl)-naphthalenetetracarboxylic-1,4:5,8-biscarboximide (NDI-2). Thermal stabilities were also measured with thermal gravimetry analyser (TGA). Naphthalene diimides showed high thermal stability. NDI derivatives exhibited good thermal stabilities that thermal decomposition peak appeared at 438 degrees C and 421 degrees C, respectively for NDI-1 and NDI-2. Highly soluble naphthalene diimide derivatives were used in inverted bulk heterojunction solar cells. Two different ZnO cathode layers were used to fabricate bulk heterojunction solar cells. One of them was single layer consists of dense ZnO layer and the other was double layer comprising porous ZnO layer onto dense ZnO layer. Inverted bulk heterojunction devices were designed in a FTO/ZnO (single or double layer)/P3HT:C-60:NDI device geometry. Best efficiency was obtained for FTO/ZnO (single or double layer)/P3HT:C-60:NDI-2 device as 8.78 mA/cm(2) of short circuit photocurrent density, 300 mV of open circuit voltage, 0.28 of filling factor, 0.74 of overall conversion efficiency. (C) 2014 Elsevier Ltd. All rights reserved.

Files

bib-0aa857d5-52e2-4115-945a-471c1d216a96.txt

Files (228 Bytes)

Name Size Download all
md5:66b36ed96939e9dc95a868e4bbc31772
228 Bytes Preview Download