Solution properties of polyaniline/carbon particle composites

This study reports on the synthesis of polymer polyaniline, a conductive polymer by nature, and the preparation of polyaniline/carbon particle (PANI/CP) composites by in situ polymerization. The solution properties and conductivities in solution of synthesized PANI and PANI/CP materials were analyzed. The viscosity of PANI and PANI/CP composite materials in N-methylpyrrolidinone (NMP) solvent at different temperatures was measured to examine their behavior in solution. Initially, the viscosity-molecular weight of PANI polymer was measured and calculated to be 78,521. The viscosities of PANI and PANI/CP composite materials decreased as the temperature increased. However, the viscosities of PANI/CP composite materials increased as the percent CP content in the composites increased. The ionic conductivities and pH changes in NMP solvent, measured at different concentrations of PANI and PANI/CP composite materials, and prepared in different ratios, were measured to investigate their behavior in solution. The ionic conductivities of PANI/CP composite materials increased as the percent CP content in the composites increased. Changes in the pH of PANI/CP composite materials decreased as the percent CP content in the composites increased. The conductivity of PANI/10% CP composite material in solution was greater than that of neat PANI polymer in solution; this indicated that CPs in PANI/10% CP composite materials made important positive contributions to the conductivities.