Visualization of one-dimensional diffusion and spontaneous segregation of hydrogen in single crystals of VO2

Hydrogen intercalation in solids is common, complicated, and very difficult to monitor. In a new approach to the problem, we have studied the profile of hydrogen diffusion in single-crystal nanobeams and plates of VO2, exploiting the fact that hydrogen doping in this material leads to visible darkening near room temperature connected with the metal-insulator transition at 65 degrees C. We observe hydrogen diffusion along the rutile c-axis but not perpendicular to it, making this a highly one-dimensional diffusion system. We obtain an activated diffusion coefficient, similar to 0.01 e(-0.6eV/kBT) cm(2) s(-1), applicable in metallic phase. In addition, we observe dramatic supercooling of the hydrogen-induced metallic phase and spontaneous segregation of the hydrogen into stripes implying that the diffusion process is highly nonlinear, even in the absence of defects. Similar complications may occur in hydrogen motion in other materials but are not revealed by conventional measurement techniques.