Preparation and Properties of Flame Retardant Poly(urethane-imide)s Containing Phosphine Oxide Moiety

The preparation of new poly(urethane-imide)s (PUIs) having acceptable thermal stability and higher flame resistance was aimed. Two new aromatic diisocyanate-containing methyldiphenylphosphine oxide and triphenylphosphine oxide moieties were synthesized via Curtius rearrangement in situ and polymerized by various prepared diols. Four aliphatic hydroxy terminated aromatic based diols were synthesized by the reaction between ethylene carbonate and various diphenolic Substances. Chemical structures of monomers and polymers were characterized by FTIR, (1)H NMR, (13)C NMR, and (31)P NMR spectroscopy. Thermal stabilities and decomposition behaviors of the PUIs were tested by DSC and TGA. Thermal measurements indicate that the polymers have high thermal stability and produce high char. Polymers exhibit quite high fire resistance, evaluated by fire test UL-94. The films of the polymers were prepared by casting the solution. Inherent viscosities, solubilities, and water absorbtion behaviors of the polymers were reported in. (C) 2009 Wiley Periodicals, Inc. J Appl Polym Sci 114:1329-1338, 2009