Spinel-Structured High Entropy Oxides: Low Temperature Synthesis, Characterization, and Potential Applications
Creators
- 1. Drexel Univ, Dept Mat Sci & Engn, Philadelphia, PA 19104 USA
- 2. Drexel Univ, Dept Chem & Biol Engn, Philadelphia, PA 19104 USA
- 3. Worcester Polytech Inst, Dept Phys, Worcester, MA 01609 USA
- 4. Cornell Univ, Robert Frederick Smith Sch Chem & Biomol Engn, Ithaca, NY 14853 USA
Description
High entropy oxides (HEOs) have recently attracted increasing attention due to their remarkable properties and relatively low cost. Herein we report a simple, highly scalable, and low temperature method for synthesizing spinel (FeNiCoCuZn)3O4 (HEO). We heated an aqueous solution containing divalent cations in high alkali environments to temperatures of 25 - 95 degrees C for 24 h under atmospheric pressure. The HEO, synthesized at 95 degrees C for 24 h in 1 M KOH, was paramagnetic at room temperature, with a magnetic mass susceptibility of chi = (7.5 +/- 0.2) x 10-7 m3kg-1. It demonstrated stable electrochemical lithium storage performance, with a gravimetric capacity of similar to 300 mAhg-1 at 100 mAg- 1. It was also active in the electrocatalytic oxygen evolution reaction with an overpotential of 460 mV in alkaline media. The band gap energies were in the range of 2.4 eV. Our advancement in the synthesis and processing of transition metal-based HEOs will undoubtedly render them a viable solution for next generation materials for energy production and storage.
Files
bib-11bf000f-9364-41aa-9f57-561b217bfdb4.txt
Files
(307 Bytes)
| Name | Size | Download all |
|---|---|---|
|
md5:12a37022f88cc3b379f3c0088362162d
|
307 Bytes | Preview Download |