Fabrication of calix[4]pyrrole nanofilms at the glassy carbon surface and their characterization by spectroscopic, optic and electrochemical methods

meso-Octamethylcalix[4]pyrrole (CP) and meso-heptaethylcalix[4]pyrrole-meso-4-aminophenyl (4APCP) modified glassy carbon (GC) electrodes were prepared by the electrochemical oxidation in acetonitrile solution. Binding of the calix[4]pyrroles with the glassy carbon surface was investigated that it is through the etheric linkage revealed from the reflection absorption infrared spectroscopy (RAIRS). Surface films of CP and 4APCP were investigated by cyclic voltammetry (CV), ellipsometry, X-ray photoelectron spectroscopy. RAIRS and the contact angle measurements. The thicknesses of the films were determined by ellipsometry which confirmed that the film was multilayer and homogeneous over the surface. Ellipsometric measurements also provided that the CP and 4APCP film thicknesses were 2.49 nm and 4.58 nm for 6 CV cycle modification, corresponding to 66 mu F/cm(2) and 106 mu F/cm(2) capacitances obtained by CV. The wetting behavior was examined by contact angle measurements and found that the hydrophobicity of the GC-4APCP surface was higher than that of GC-CP, probably due to the aromatic meso substituent present in the former. (C) 2010 Elsevier B.V. All rights reserved.