Oxygen vacancies on Pd/TiO2 are detected at low pressures by ESR spectroscopy at ambient temperatures

A low field benchtop electron spin resonance (ESR) (also referred to as electron paramagnetic resonance (EPR)) spectrometer is used to reveal paramagnetic centres such as oxygen vacancies and Ti+3 centres over 0.5%Pd/TiO2. The measurement was performed at room temperature after the sample was reduced in situ under mild hydrogen pressures and evacuated to P < 10(-6 )Torr. The measurement was possible due to a T-1 compensation effect under vacuum: Correlation times at low pressures enabled sufficient line narrowing and detection of the ESR signal, justifying a method using benchtop spectrometers coupled to vacuum manifolds. The method justification was demonstrated using similar measurements performed on a reference compound, Mn(II) in plasticine: a measurement performed by saturation recovery technique revealed that T-1 of the signal due to Mn(II) was smaller in vacuum than its atmosphere exposed counterpart. By applying vacuum, the ESR spectra of 0.5%Pd/TiO2 were collected at ambient temperatures, with features equivalent to the published data obtained at cryogenic temperatures.