Understanding the effect of Ni content on microstructure and mechanical properties of A384 HPDC alloy

Investigations have been carried out to understand the correlation between Ni content and properties of HPDC cast A384 aluminium alloy in as-cast and heat-treated conditions. Depending on Ni content in the alloy, different Ni-bearing intermetallics were formed. Suitable heat treatment conditions were selected after a series of experiments to obtain optimal mechanical properties. Most of the Ni containing inter-metallics found to be stable at solutionizing temperatures which have a dramatic effect on the mechanical properties of alloys after natural and artificial aging. The results showed that, after heat treatment, to achieve higher strength values lower Ni additions are favourable. (c) 2021 Published by Elsevier B.V.