Enhanced bonding of biomimetic apatite coatings on surface-modified titanium substrates by hydrothermal pretreatment

The biomimetic coating method was employed by soaking the titanium substrates in a 1.5X simulated body fluid (1.5XSBF). Calcium was implanted on the cleaned titanium surfaces under four different hydrothermal conditions before exposure to SBF. For this purpose, the substrates were immersed in aqueous solutions of CaO at 0.02 or 0.2 mol/L concentrations for 1 or 8 h in the temperature-controlled hydrothermal chamber kept at 230 degrees C. The effects of hydrothermal solution concentration and immersion time on the substrate surfaces were assessed in terms of coating integrity. All the modified substrates were able to develop B-type hydroxy-carbonate apatite coatings. It was found that the titanium substrates pretreated for 8 h developed on their surfaces well-adhering and scattered Ca(OH)(2) crystals that contributed to roughness. The apatite coatings on such substrates exhibited higher bond strength compared to the coatings on the relatively "smoother" substrates (i.e., pretreated for 1 h). The mean values for tensile and shear strengths increased up to 22.4 +/- 3.2 and 9.7 +/- 2.7 MPa, respectively, for the mechanical test specimens prepared by soaking the substrates, which were pretreated for 8 h in the 0.2 mol/L CaO solution, in the SBF for 2 weeks. (c) 2013 Elsevier B.V. All rights reserved.