Preparation of polypyrrole/multi-walled carbon nanotube hybrids by electropolymerization combined with a coating method for counter electrodes in dye-sensitized solar cells

In this work, multi-wall carbon nanotubes coated with polypyrrole (PPy/MWCNT) have been used as counter electrode (CE) materials for dye-sensitized solar cells (DSSCs). PPy was deposited onto fluorine-doped tin-oxide-coated glass by electrochemical polymerization of pyrrole. Three surfactants were used in the preparation of the hybrids: cationic cetyltrimethylammonium bromide, anionic sodium dodecylbenzenesulfonate (DBSNa), and non-ionic polyoxyethylene sorbitan monolaurate (Tween20). The morphologies of the PPy and PPy/MWCNT hybrids were investigated using scanning electron spectroscopy. Chemical composition of the prepared CEs was determined by X-ray photoelectron spectroscopy and Fourier-transformed infrared spectroscopy. The catalytic activity of the PPy and PPy/MWCNT layers was evaluated using cyclic voltammetry, and the photovoltaic properties of DSSCs with PPy and PPy/MWCNT CEs were characterized using I-V measurements. PPy/MWCNT samples that were prepared by electrochemical polymerization showed the best results when the anionic surfactant DBSNa was used during polymerization. The photoelectric conversion efficiency of PPy/MWCNT prepared by electrochemical polymerization was 2.9%, which was 59% of that of Pt CE (4.9%).