Ahangari, Mohammad; Mostafaei, Jafar; Zakerifar, Hamid; Sayyah, Ali; Delibas, Nagihan; Coruh, Ali; Mahmoudi, Elham; Asghari, Elnaz; Niaei, Aligholi
La0.8Sr0.2Cu0.4Mn0.6O3 (LSCM0.6) and La0.8Sr0.2Cu0.7Mn0.3O3 (LSCM0.3) were prepared and Pd (10 % mole in B site) was partial substituted in the B site, with the aim of investigating their performance as supercapacitor electrodes. The crystal structure, morphology and electrochemical activity of them studied in details. LSCM0.3 has a cubic structure and belongs to the Pm-3 m space group. The partial substitution of Pd in B site, increased the distortion of the structure and oxygen vacancies. La0.8Sr0.2(Cu0.4Mn0.6)(0.9)Pd0.1O3 (LSCMP0.6) recognized to be the best sample of the synthesized. This sample showed obvious pseudo-capacitive behavior and the highest specific capacitance (113 F.g(-1)) at a current density of 1 A.g(-1). The improved electrochemical activity of LSCMP0.6 were originated from the structural features and higher oxygen vacancy content. Extensive charge-discharge cycles performed to assess the electrochemical stability of LSCMP0.6. It was found, after 3000 charge-discharge cycles, the specific capacitance dropped to about 70 % of its initial value.
Dosya adı | Boyutu | |
---|---|---|
bib-6afbabed-13ad-437b-8b94-41931abeebd9.txt
md5:0f25341a0dc46454cd8c8ea0227cc1a3 |
434 Bytes | İndir |
Görüntülenme | 0 |
İndirme | 0 |
Veri hacmi | 0 Bytes |
Tekil görüntülenme | 0 |
Tekil indirme | 0 |