Ulker, Damla; Neal, Thomas J.; Crawford, Aileen; Armes, Steven P.
RAFT solution polymerization is used to polymerize 2-hydroxypropyl methacrylate (HPMA). The resulting PHPMA precursor is then chain-extended using N,N '-dimethylacrylamide (DMAC) to produce a series of thermoresponsive PHPMA-PDMAC diblock copolymers. Such amphiphilic copolymers can be directly dispersed in ice-cold water and self-assembled at 20 degrees C to form spheres, worms, or vesicles depending on their copolymer composition. Construction of a pseudo-phase diagram is required to identify the pure worm phase, which corresponds to a rather narrow range of PDMAC DPs. Such worms form soft, free-standing gels in aqueous solution at around ambient temperature. Rheology studies confirm the thermoresponsive nature of such worms, which undergo a reversible worm-to-sphere on cooling below ambient temperature. This morphological transition leads to in situ degelation, and variable temperature H-1 NMR studies indicate a higher degree of (partial) hydration for the weakly hydrophobic PHPMA chains at lower temperatures. The trithiocarbonate end-group located at the end of each PDMAC chain can be removed by treatment with excess hydrazine. The resulting terminal secondary thiol group can form disulfide bonds via coupling, which produces PHPMA-PDMAC-PHPMA triblock copolymer chains. Alternatively, this reactive thiol group can be used for conjugation reactions. A PHPMA(141)-PDMAC(36) worm gel was used to store human mesenchymal stem cells (MSCs) for up to three weeks at 37 degrees C. MSCs retrieved from this gel subsequently underwent proliferation and maintained their ability to differentiate into osteoblastic cells.
Dosya adı | Boyutu | |
---|---|---|
bib-104441c7-61b7-4e0a-b4e8-ed09eea1f213.txt
md5:c74ddbe1c1cf5f49e7f7b0495e370480 |
282 Bytes | İndir |
Görüntülenme | 0 |
İndirme | 0 |
Veri hacmi | 0 Bytes |
Tekil görüntülenme | 0 |
Tekil indirme | 0 |